Iron-based superconductors, which were discovered only about four years ago, are a hot research topic, in part because they are more amenable to commercial applications than copper-based superconductors, which are more difficult to make and are frequently brittle. Of the four broad classes of iron-based superconductors, the 1:2:2 class -- so named because their crystals are built around a hub of one atom of calcium, two of iron and two of arsenic -- is particularly promising because these superconductors' properties can be custom-tailored by substituting other atoms for these basic elements.
Magnets made with low-temperature superconductors have already found use in hospital MRI machines, but less expensive MRI machines and other applications, such as superconducting cables for resistance-free power transmission over long distances, become closer to reality the more choices manufacturers have among superconductors.
Working at the NIST Center for Neutron Research (NCNR) and the University of Maryland, the team found that a particular type of 1:2:2 superconductor possesses some unexpected properties. Of perhaps greatest value to manufacturers is that its threshold temperature of superconductivity is 47 degrees Kelvin, the highest yet for the 1:2:2 class, whose previous record was 38K.
But the crystal also has a highly curious property: It can superconduct at this record temperature when a smaller atom is substituted for the crystal's original calcium in some of its hubs, and when this substitution is performed, the overall crystal actually shrinks by about 10 percent, a dramatic size change. "It's almost like what would happen if you cut off a few inches from the bottom of your chair's legs," says the NCNR's Jeff Lynn. "The crystal just collapses. The change is quite visible in neutron scans."
This effect is likely one that manufacturers will want to avoid. But Lynn says the group's research has determined how to make the substitution while eluding the collapsed state altogether, so that as it is cooled, the potential mechanical instabilities associated with the collapse are sidestepped. "This understanding should enable manufacturers to use the superconductor in electronic devices," he says.